316 stainless steel , 18Cr-12Ni-2.5Mo, Hebei Maishi wire mesh products 316 stainless steel , adding Mo, therefore corrosion resistance, resistance to atmospheric corrosion and high temperature strength in particular, can be used in harsh conditions ; hardening excellent ( non-magnetic ) .

Material: AISI304, AISI304L, AISI310, AISI310S, AISI316, AISI316L, AISI317, refer Stainless Steel Wire Mesh Alloys
More about 316 stainless steel, please click: Marine Grade Stainless Steel Mesh

1.MaiShi wire mesh products 316 stainless steel: Chemical composition

Chemical composition/%
Brand	C	Si	Mn	P	S	Ni	Cr	Mo	N	Other
316	≤0.08	≤1	≤2	≤0.045	≤0.030	10.0~14.0	16.0~18.0	2.00~3.00	-

2.MaiShi wire mesh products 316 stainless steel：Mechanical Properties

Brand	Heat treatment	The yield strength σ0.2/Mpa	Tensile strength σb/Mpa	Elongation δ5/%	HBS	HRB	HV
316	1010~1120 Fast cooling	≥205	≥520	≥40	≤187	≤90	≤200

3.Heat resistance of 316 stainless steel

At 871°C intermittent use (1600°F) or less , and at 927C°(1700°F) or more continuous use, Hebei Maishi wire mesh products 316 stainless steel (06Cr17Ni12Mo2), with good resistance to oxidation . In the range of 427°C-857°C (800°F-1575°F) , preferably not continuous use 316 stainless steel , but when the temperature is outside the range of continuous use 316 stainless steel which has good heat resistance. Hebei Maishi wire mesh products 316L stainless steel, resistant to the performance of the carbide precipitation, and better than the 316 stainless steel, can be used in the above temperature range.

4.Heat treatment of 316 stainless steel

In the temperature range 1850-2050°F, annealing, then rapid annealing, rapid cooling. Hebei Maishi wire mesh prompts you, 316 stainless steel cannot be hardened by heat treatment.

5.Welded 316 stainless steel

Hebei Maishi wire mesh products 316 stainless steel, with good weldability. To be able to use all the standard welding method to weld. Welding according to use , respectively 316Cb, 316L stainless steel or 309Cb filler rod or electrode welding. For optimum corrosion resistance , 316 stainless steel welding section, the need for annealing treatment after welding. Hebei Maishi wire mesh prompts you, if you use 316L stainless steel , does not need to be annealed after welding.

6. Typical use of 316 stainless steel

Hebei Maishi wire mesh products 316 stainless steel, widely used in the pulp and paper equipment heat exchangers, dyeing equipment , film processing equipment , piping, exterior building materials used in coastal areas . 2013 Hebei Maishi wire mesh products 316 stainless steel should solenoid valve areas , mainly for housing , hoop , ball , valve , valve seat, nut, stem and so on.